Wet chemical isotropic etching procedures of silicon: a possibility for the production of deep-structured microcomponents
Author(s): Norbert Schwesinger; Arne Albrecht
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

We have observed the etch rate and the underetch rate of <100>-, <110>-, and <111>- oriented silicon substrates in isotropic etching solutions. We have studied the influence of the composition of the solution and the temperature on the etch rates. Further we also have examined the stability of different masking materials. The stability of thermally grown SiO2 is very poor. Silicon nitride films show a comfortable stability at low etching temperatures. The stability of these films decreases with significant differences depending on the deposition temperature. The best stability were found with metal masks and photoresist masks. The values of the etch rates were in a range between 1 micrometer/min and about 900 micrometers/min. A controlled procedure could be achievable up to etch rates of about 100 micrometers/min. The etch rates and the undercut rates as well as the etch rates of the differently oriented materials are different under the same process conditions. In some cases we found profiles that are known from anisotropic dry etching procedures. All achieved results indicate an anisotropic etching behavior of silicon in etchants based on compositions of HNO3-HF-H2O.

Paper Details

Date Published: 5 September 1997
PDF: 8 pages
Proc. SPIE 3223, Micromachining and Microfabrication Process Technology III, (5 September 1997); doi: 10.1117/12.284467
Show Author Affiliations
Norbert Schwesinger, Technische Univ. Ilmenau (Germany)
Arne Albrecht, Technische Univ. Ilmenau (Germany)


Published in SPIE Proceedings Vol. 3223:
Micromachining and Microfabrication Process Technology III
Shih-Chia Chang; Stella W. Pang, Editor(s)

© SPIE. Terms of Use
Back to Top