Influence of defects on photoluminescence in C60 crystals
Author(s): Masaru Tachibana; Kazuki Nishimura; Takeshi Komatsu; Takaaki Sunakawa; Kenichi Kojima
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Photoluminescence spectra of C60 crystals with high quality was measured before and after the mechanical deformation . New peak at 685 nm appeared after the deformation. The peak was observed only at temperatures lower than about 90 K, where its intensity decrease with increasing temperature. The temperature dependence of the peak intensity was correlated with that of main other peak at 735 nm, which would originate in intrinsic C60 crystals. From these result, the origin of the peak at 685 nm is discussed in the light of crystal defects, especially dislocations.

Paper Details

Date Published: 1 November 1997
PDF: 7 pages
Proc. SPIE 3142, Fullerenes and Photonics IV, (1 November 1997); doi: 10.1117/12.279250
Show Author Affiliations
Masaru Tachibana, Yokohama City Univ. (Japan)
Kazuki Nishimura, Yokohama City Univ. (Japan)
Takeshi Komatsu, Yokohama City Univ. (Japan)
Takaaki Sunakawa, Yokohama City Univ. (Japan)
Kenichi Kojima, Yokohama City Univ. (Japan)


Published in SPIE Proceedings Vol. 3142:
Fullerenes and Photonics IV
Zakya H. Kafafi, Editor(s)

© SPIE. Terms of Use
Back to Top