Sm2+-doped silicate glasses: sol-gel processing and persistent spectral hole burning
Author(s): Masayuki Nogami; Yoshihiro Abe
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Sm2+-doped glasses in the system of Al2O3-SiO2 were prepared by the sol-gel processing of metal alkoxides and the reaction with H2 gas at 800 degrees Celsius, of which hole burning properties were investigated. Sm3+ ions-containing glasses prepared by a sol-gel method were reacted with H2 gas to form the Sm2+ ions. Fluorescence line narrowing spectra of the 5D0 yields 7F1 transition were analyzed to study the local structure surrounding the Sm2+ ion. It is concluded that the Sm2+ ions are closely coordinated with nine oxygens of the AlO6 group in aluminosilicate glasses and the addition of Al3+ ions into glass induces an increase in the coordination number of the Sm2+. The fluorescence intensity of the Sm2+ and Sm3+ ions considerably increases in glasses containing more than 5 mol% Al2O3. The holes were burned in the 7F0 yields 5D0 line of the Sm2+ ions using a DCM dye laser at 77 K. The hole depth increased with increasing the laser irradiation time, reaching up to approximately 15% of the total intensity within a few hundred seconds. The hole width was 3 cm-1 full width at half maximum at 77 K and increased with increasing temperature.

Paper Details

Date Published: 2 October 1997
PDF: 7 pages
Proc. SPIE 3136, Sol-Gel Optics IV, (2 October 1997); doi: 10.1117/12.279162
Show Author Affiliations
Masayuki Nogami, Nagoya Institute of Technology (Japan)
Yoshihiro Abe, Nagoya Institute of Technology (Japan)


Published in SPIE Proceedings Vol. 3136:
Sol-Gel Optics IV
Bruce S. Dunn; John D. Mackenzie; Edward J. A. Pope; Helmut K. Schmidt; Masayuki Yamane, Editor(s)

© SPIE. Terms of Use
Back to Top