Preparation and characterization of super-water-repellent Al2O3 coating films with high transparency
Author(s): Tsutomu Minami; Noriko Katata; Kiyoharu Tadanaga
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Alumina thin films with a roughness of 20 to 50 nm were formed by immersing the porous alumina gel films prepared by the sol- gel method in boiling water. When hydrolyzed fluoroalkyltrimethoxysilane was coated on the alumina films, the films showed super-water-repellency and high transparency; the contact angle for water of the film was 165 degrees and the transmittance for visible light was higher than 92%. When the fluoroalkyltrimethoxysilane-coated thin films were heat- treated at temperatures higher than 500 degrees Celsius, the films became super-hydrophilic; the contact angle for water on the films was less than 5 degrees. It was shown the existence of air in the pores on the surface caused the super-water- repellency and that of water in the pores caused the super- hydrophilic property. The transparent, super water-repellent and super-hydrophilic coating films formed on glasses, metals, and ceramics have practical applications such as optical lenses, eye-glasses, cover glasses for solar cells, windshields of automobiles, and so on.

Paper Details

Date Published: 2 October 1997
PDF: 8 pages
Proc. SPIE 3136, Sol-Gel Optics IV, (2 October 1997); doi: 10.1117/12.279158
Show Author Affiliations
Tsutomu Minami, Osaka Prefecture Univ. (Japan)
Noriko Katata, Osaka Prefecture Univ. (Japan)
Kiyoharu Tadanaga, Osaka Prefecture Univ. (Japan)


Published in SPIE Proceedings Vol. 3136:
Sol-Gel Optics IV
Bruce S. Dunn; John D. Mackenzie; Edward J. A. Pope; Helmut K. Schmidt; Masayuki Yamane, Editor(s)

© SPIE. Terms of Use
Back to Top