Blue emission dye doped polymer-based electroluminescent devices for display
Author(s): Haiyan An; Shanhua Xue; Baijun Chen; Jingying Hou; Jingsong Huang; Shiyong Liu; Jiaqi Yu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Low operating voltage organic molecule dye doped polymers blue electroluminescent (EL) devices were constructed by using air stable aluminum as cathode 1,1,4,4,-tetraphenyl- 1,3-butadiene (TPB) doped poly (N-Vinylcarbazole) (PVK) was used as the light emitting layer, and a layer of tris(8- quinolinolate)-Aluminum(Alq3) film worked as an electron-transporting layer. A device with two layer structure of indium-tin-oxide(ITO)/TPB:PVK/Alq3/Al was obtained. Blue emission began at DC bias voltage of 3.5 V, and blue electroluminescence of 500 cd/m2 was observed at about 10 V, the EL peak was at 449 nm. By using Al as cathode, 2-(4-biphenylyl)-5-(4-terbutypheny)-1-3,4- oxadiazole(PBD) as hole-blocking layer, the device with the structure of ITO/TPB:PVK/PBD/Alq3/Al was also fabricated. Blue emission began at 4 V, more than 1000 cd/m2 was observed at 14 V. These are among the lowest known operating voltage for polymeric EL devices using air stable electrodes. The characteristics of these two kinds of structure devices have also been investigated.

Paper Details

Date Published: 30 September 1996
PDF: 5 pages
Proc. SPIE 2892, Display Devices and Systems, (30 September 1996); doi: 10.1117/12.253348
Show Author Affiliations
Haiyan An, Jilin Univ. (China)
Shanhua Xue, Jilin Univ. (China)
Baijun Chen, Jilin Univ. (China)
Jingying Hou, Jilin Univ. (China)
Jingsong Huang, Jilin Univ. (China)
Shiyong Liu, Jilin Univ. (China)
Jiaqi Yu, Changchun Institute of Physics (China)