Improvement in NEDT characteristics of InAs/GaAs quantum dot based 320x256 focal plane array implanted with hydrogen ions
Author(s): S. Upadhyay; D. P. Panda; D. Das; N.B.V. Subrahmanyam; P. Bhagwat; S. Chakrabarti
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

In this work, we demonstrate two times enhancement in NEDT response of InAs/InGaAs/ GaAs dot-in-the-well (DWELL) structure implanted with hydrogen ions of 3 MeV energy and 5×1012 ions/cm2 fluence. Low temperature photoluminescence study shows emission peak at 1130 nm which corresponds to ground state transition between conduction to valence band. PL enhancement is observed in all hydrogen implanted samples indicating the passivation of defects/dislocations in the vicinity of QDs and surrounding layer. The spectral response peak was observed at 5 μm corresponding to the intersubband transition and measured upto 76 K. Next, 320×256 format infrared FPA was fabricated involving multistage lithography, wet etching, metal stack and bump deposition. The NEDT parameter, which represents minimum temperature difference that FPA based camera can resolve, improved from 239 mK( as-grown) to 129 mK ( implanted sample).

Paper Details

Date Published: 14 May 2018
PDF: 6 pages
Proc. SPIE 10624, Infrared Technology and Applications XLIV, 1062423 (14 May 2018); doi: 10.1117/12.2305069
Show Author Affiliations
S. Upadhyay, Indian Institute of Technology Bombay (India)
D. P. Panda, Indian Institute of Technology Bombay (India)
D. Das, Indian Institute of Technology Bombay (India)
N.B.V. Subrahmanyam, Bhabha Atomic Research Ctr. (India)
P. Bhagwat, Bhabha Atomic Research Ctr. (India)
S. Chakrabarti, Indian Institute of Technology Bombay (India)


Published in SPIE Proceedings Vol. 10624:
Infrared Technology and Applications XLIV
Bjørn F. Andresen; Gabor F. Fulop; Charles M. Hanson; John Lester Miller; Paul R. Norton, Editor(s)

© SPIE. Terms of Use
Back to Top