The role of silanized and capped with TiO2 gold nanorods of different aspect ratios in co-sensitized DSSCs for transparent windows applications
Author(s): Marina Mazzoni; Lorenzo Zani; Janardan Dagar; Sarah Lai; Sonia Centi; Roberto Pini; Fulvio Ratto
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Gold nanarods (GNRs) with an aspect ratio equal to 3:1 and 4:1 and a major axis equal to 50 nm, silanized and capped with titania (c-GNRs), were embedded within the 6μ thick semiconductor layer of DSSCs based on an organic D-π-A sensitizer dye (L0 or L1) and a squaraine co-sensitizer (SQ2). These dye cocktails and a transparent titania paste were selected to maximize the transmittance of DSSCs in a region of maximum visual acuity. The thickness of the SiO2 layer was consisted of about 4.0 nm and that of the TiO2 layer of about 2.0 nm in order to maintain high the localized surface plasmon resonance (SPR) effects produced by GNRs and to prevent Au corrosion. The slight thickness of both types of capping was not sufficient to preserve the dimensions of the gold nanorods during sintering at 450 °C. Absorbance, transmittance and reflectance spectra of the films were measured after they were dyed. The plasmonic effects were distinguishable both in absorbance and absorptance spectra for all the types of dyes cocktails and GNRs aspect ratios used. Transmittance values depended on the cocktail used and on the adsorption of the dyes on the semiconductor film blended with c-GNRs. When the mix of L1 and SQ2 was used together with GNRs of a 3:1 aspect ratio, we achieved an increase of 23% in DSSC efficiency (from 3.50% to 4.32%) but transmittance values higher than 50% only between 560 nm and 630 nm.

Paper Details

Date Published: 16 February 2018
PDF: 6 pages
Proc. SPIE 10527, Physics, Simulation, and Photonic Engineering of Photovoltaic Devices VII, 105270X (16 February 2018); doi: 10.1117/12.2289552
Show Author Affiliations
Marina Mazzoni, CNR-Istituto di Fisica Applicata "Nello Carrara" (Italy)
Lorenzo Zani, CNR-Istituto di Chimica dei Composti OrganoMetallici (Italy)
Janardan Dagar, Univ. degli Studi di Roma "Tor Vergata" (Italy)
Sarah Lai, CNR-Istituto di Fisica Applicata "Nello Carrara" (Italy)
Sonia Centi, CNR-Istituto di Fisica Applicata "Nello Carrara" (Italy)
Roberto Pini, CNR-Istituto di Fisica Applicata "Nello Carrara" (Italy)
Fulvio Ratto, CNR-Istituto di Fisica Applicata "Nello Carrara" (Italy)


Published in SPIE Proceedings Vol. 10527:
Physics, Simulation, and Photonic Engineering of Photovoltaic Devices VII
Alexandre Freundlich; Laurent Lombez; Masakazu Sugiyama, Editor(s)

© SPIE. Terms of Use
Back to Top