Tailoring Nd3+ emission spectrum by a neodymium-doped tellurite all-solid photonic bandgap fiber
Author(s): Hoang Tuan Tong; Daisuke Demichi; Takenobu Suzuki; Yasutake Ohishi
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A tellurite all-solid photonic bandgap fiber (ASPBF) whose cladding consists of 60 high-index rods arranged periodically around a central core was successfully fabricated. The diameter of high-index rod was about 5.0 μm and the distance between the center of two adjacent high-index rods was approximately 8.0 μm. The high-index rod was made of the TeO2-Li2O-WO3-MoO3-Nb2O5 (TLWMN) glass, the cladding was made of the TeO2-ZnO-Na2O-La2O3 (TZNL) glass as the background glass material and the central core was made of TZNL glass doped with 0.5 wt% of Nd2O3. A supercontinuum light from 0.6 to 2.4 μm was coupled into the core of fiber which is 2.2 cm long to measure its transmission spectrum. High transmission bands were obtained in the vicinity of 0.75 and 1.3 μm but the transmission was suppressed in the wavelength range from 1.0 to 1.06 μm. When a titanium∶Sapphire laser source at 0.75 μm was used, the emission spectrum was obtained with two peaks at 1.06 and 1.33 μm which are attributed to the 4F3/24I11/2 and 4F3/24I13/2 transitions of Nd3+ ion, respectively. The intensities of those emission peaks were compared with those obtained from a bulk glass having the same doping concentration of Nd3+. The results showed that by using tellurite ASPBF, the intensity of the 1.06-μm emission was suppressed by one-twelfth but the intensity of the 1.33-μm emission was maintained. This feature is very advantageous to filter out the 1.06-μm emission of Nd3+ ion in order to realize practical amplifier devices at 1.3 μm.

Paper Details

Date Published: 22 February 2018
PDF: 6 pages
Proc. SPIE 10528, Optical Components and Materials XV, 105281P (22 February 2018); doi: 10.1117/12.2289280
Show Author Affiliations
Hoang Tuan Tong, Toyota Technological Institute (Japan)
Daisuke Demichi, Toyota Technological Institute (Japan)
Takenobu Suzuki, Toyota Technological Institute (Japan)
Yasutake Ohishi, Toyota Technological Institute (Japan)


Published in SPIE Proceedings Vol. 10528:
Optical Components and Materials XV
Shibin Jiang; Michel J. F. Digonnet, Editor(s)

© SPIE. Terms of Use
Back to Top