Far-side geometrical enhancement in surface-enhanced Raman scattering with Ag plasmonic films
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Surface-enhanced Raman scattering (SERS) is a surface sensitive technique where the large increase in scattering has primarily been attributed to electromagnetic and chemical enhancements. While smaller geometrical enhancements due to thin film interference and cavity resonances have also been reported, an additional enhancement in the SERS signal, referred to as the ‘far-side geometrical enhancement’, occurs when the SERS substrate is excited through an underlying transparent dielectric substrate. Here the far-side geometrically-enhanced SERS signal has been explored experimentally in more detail. Thermally evaporated Ag plasmonic films functionalised with thiophenol were used to study the dependence of the geometrically-enhanced SERS signal on the excitation wavelength, supporting substrate material and excitation angle of incidence. The results were interpreted using a ‘geometrical enhancement factor’ (GEF), defined as the ratio of far-side to near-side SERS signal intensity. The experimental results confirmed that the highest GEFs of 3.2-3.5× are seen closer to the localized surface plasmon resonance peak of the Ag metallic nanostructures. Interestingly, the GEF for Ag plasmonic films deposited on glass and sapphire were the same within the measurement errors, whereas increasing angle of incidence showed a decrease in the GEF. Given this improved understanding of the far-side geometrical SERS enhancement, the potential for further signal amplification and optimisation for practical sensing applications can now be considered, especially for SERS detection modes at the farend of optical fibre probes and through process windows.

Paper Details

Date Published: 2 January 2018
PDF: 12 pages
Proc. SPIE 10456, Nanophotonics Australasia 2017, 104564X (2 January 2018); doi: 10.1117/12.2283335
Show Author Affiliations
M. Nilusha M. N. Perera, Swinburne Univ. of Technology (Australia)
W. E. Keith Gibbs, Swinburne Univ. of Technology (Australia)
Saulius Juodkazis, Swinburne Univ. of Technology (Australia)
Paul R. Stoddart, Swinburne Univ. of Technology (Australia)


Published in SPIE Proceedings Vol. 10456:
Nanophotonics Australasia 2017
James W. M. Chon; Baohua Jia, Editor(s)

© SPIE. Terms of Use
Back to Top