Author(s): Sheldon M. Smith
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

In addition to the ambient condition tape test, five mechanical tests of the IR-black coating, Ames 24E2, were performed at either liquid helium or liquid nitrogen teperatures. Tensile strain in the coating at liquid nitrogen temperature was measured up to values of 4E-3, both before and after the coating was cycled down to liquid helium temperature. When applied to an aluminum substrate which was then bent in liquid nitrogen, the aluminum substrate always failed (permanently deformed) well before the coating failed. Sinusoidal accelerations up to 45 Gs in liquid nitrogen and 25 Gs in liquid helium did not crack or otherwise visibly damage the coating. Both sinusoidal and random acceleration at about 90 K of a representative baffle vane structure, at frequencies from 10 to 2000 Hz and up to 15 Gs, did not damage the coating, even at the intersection of a baffle with the telescope tube. Thus on a macroscopic level, cryogenic cooling and various levels of acceleration and strain did not affect this coating. However, on a microscopic scale, some loose particles were found associated with several tests. Outgassing data are also given.

Paper Details

Date Published: 1 December 1990
PDF: 8 pages
Proc. SPIE 1331, Stray Radiation in Optical Systems, (1 December 1990); doi: 10.1117/12.22659
Show Author Affiliations
Sheldon M. Smith, NASA/Ames Research Ctr. (United States)

Published in SPIE Proceedings Vol. 1331:
Stray Radiation in Optical Systems
Robert P. Breault, Editor(s)

© SPIE. Terms of Use
Back to Top