Recent development status of rinse material for EUV lithography
Author(s): Kazuma Yamamoto; Maki Ishii; Tomoyasu Yashima; Tatsuro Nagahara
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Extreme ultraviolet lithography is one of the promising high volume manufacturing processes for devices below 7 nm node and beyond. However, resist pattern collapse is one of the hurdles in achieving a comfortable process margin/window for resist patterning. To suppress this resist pattern collapse and to improve manufacturing process margin, undoubtedly it is a well-known fact that the rinse materials can mitigate a pattern collapse at development process.

In this study, we focus on the relationship between resist swelling and pattern collapse, based on the assumption of resist pattern softening induced by resist swelling and further resist pattern bending or deformation which could be classified as pattern collapse. To verify this model, two samples of Rinse-A and Rinse-B which showed similar capillary force but different resist swelling behavior expected, respectively, were prepared. And the hardness of the resist films treated using those rinse materials together with de-ionized water as reference rinse, were measured using nano-indentation measurement technique.

From the result, it was found that Rinse-A had the resist film hardness reduced by 7.9 % as compared to that on de-ionized water. On the other hand, Rinse-B which was designed to suppress the penetration of additives into the resist film, exhibited comparable hardness property to that on reference rinse, de-ionized water. Finally, the evaluation of lithographic performance of the photoresist in different rinse process conditions using Rinse-A and Rinse-B was carried out, and Rinse- B achieved 12.7 nm minimum pattern size of resist feature at 16 nm half pitch printing by interference projection system on Extreme Ultraviolet lithography, whereas Rinse-A showed 16.5 nm.

Paper Details

Date Published: 5 May 2017
PDF: 7 pages
Proc. SPIE 10143, Extreme Ultraviolet (EUV) Lithography VIII, 101431X (5 May 2017); doi: 10.1117/12.2257393
Show Author Affiliations
Kazuma Yamamoto, Merck Performance Materials Ltd. (Japan)
Maki Ishii, Merck Performance Materials Ltd. (Japan)
Tomoyasu Yashima, Merck Performance Materials Ltd. (Japan)
Tatsuro Nagahara, Merck Performance Materials Ltd. (Japan)


Published in SPIE Proceedings Vol. 10143:
Extreme Ultraviolet (EUV) Lithography VIII
Eric M. Panning, Editor(s)

© SPIE. Terms of Use
Back to Top