Graded index materials by the sol-gel process
Author(s): Masayuki Yamane; Atsuo Yasumori; Mitsunobu Iwasaki; Kazutaka Hayashi
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A gradient-index glass rod of about 13 mm in diameter and 20 mm in length with the refractive index difference of about 0.05 between center and perimeter has been prepared by the sol-gel process from a precursor solution consisted of tetramethoxysilane, tetraethoxysilane, boron ethoxide and aqueous solution of lead acetate. A bubble free wet gel of about 35 mm in diameter and 50 mm in length was obtained by adding acetic acid to the precursor solution as a buffering agent. The liquid in the micropores of the wet gel was totally replaced with acetone. Then the compositional gradient of lead was formed in radial direction of the gel by soaking in an ethanolic solution of potassium acetate. A transparent r-GRIN rod of about 13 mm in diameter was obtained by sintering the gel at 550°C.

Paper Details

Date Published: 1 November 1990
PDF: 12 pages
Proc. SPIE 1328, Sol-Gel Optics, (1 November 1990); doi: 10.1117/12.22553
Show Author Affiliations
Masayuki Yamane, Tokyo Institute of Technology (Japan)
Atsuo Yasumori, Tokyo Institute of Technology (Japan)
Mitsunobu Iwasaki, Tokyo Institute of Technology (Japan)
Kazutaka Hayashi, Tokyo Institute of Technology (Japan)


Published in SPIE Proceedings Vol. 1328:
Sol-Gel Optics
John D. Mackenzie; Donald R. Ulrich, Editor(s)

© SPIE. Terms of Use
Back to Top