Proceedings Paper

Optical coating uniformity of 200mm (8") diameter precut wafers
Author(s): Travis C. Burt; Mark Fisher; Dean Brown; David Troiani
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Automated spectroscopic profiling (mapping) of a 200 mm diameter near infrared high reflector (centered at 1064 nm) are presented. Spatial resolution at 5 mm or less was achieved using a 5 mm × 1.5 mm monochromatic beam. Reflection changes of 1.0% across the wafer diameter were observed under s-polarized and p- polarized conditions. Redundancy was established for each chord by re-measuring the center of the wafer and reproducibility of approximately <0.1% was demonstrated by duplicate measurements. These measurements demonstrate informative spatial spectroscopic information can be obtained on large diameter samples. Multi-angle Photometric Spectroscopy (MPS) was used to measure the reflectance and transmittance of a sample across a range of angles (θi) at near normal angles of incidence (AOI). A recent development by Agilent Technologies, the Cary 7000 Universal Measurement Spectrophotometer (UMS) combines both reflection and transmission measurements from the same patch of a sample’s surface in a single automated platform for angles of incidence in the range 5°≤|θi|≤85° (i.e. angles on either side of beam normal noted as +/-). We describe the use of MPS on the Cary 7000 UMS with rotational (Φ) and vertical (z) sample positioning control. MPS(θi,Φ,z) provides for automated unattended multi-angle R/T analysis of at 200 mm diameter samples with the goal to provide better spectroscopic measurement feedback into large wafer manufacturing to ensure yields are maximized, product quality is better controlled and waste is reduced before further down-stream processing.

Paper Details

Date Published: 20 February 2017
PDF: 7 pages
Proc. SPIE 10110, Photonic Instrumentation Engineering IV, 101100J (20 February 2017); doi: 10.1117/12.2254267
Show Author Affiliations
Travis C. Burt, Agilent Technologies Australia (Australia)
Mark Fisher, Agilent Technologies, Inc. (United States)
Dean Brown, Agilent Technologies, Inc. (United States)
David Troiani, Agilent Technologies, Inc. (United States)


Published in SPIE Proceedings Vol. 10110:
Photonic Instrumentation Engineering IV
Yakov G. Soskind; Craig Olson, Editor(s)

© SPIE. Terms of Use
Back to Top