Effect of iodine pressure in the sensitization treatment on the structural and electrical properties of PbSe films
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Influence of iodine vapor pressure during the sensitization process on the morphology, microstructure, and electrical properties of the PbSe films was studied. PbSe films of polycrystalline particles were coated on thermally oxidized silicon substrates by chemical bath deposition using a solution of lead acetate and sodium selenosulfate without or with iodine-doping. As-grown PbSe films were oxidized at 380°C for 30 min and then treated with iodine vapor of different pressures at 380 °C for 5 min. As the iodine vapor pressure was increased above 20 Pa during the iodination process, the PbI2 phase begins to form in the undoped films, while the PbI2O2 and Pb3O4 phases as well as PbI2 are formed in the iodine-doped films. Only iodine-doped films showed photo response. The sheet resistance and the signal to noise ratio increased with the iodine vapor pressure up to the 17.5 Pa iodine pressure. The role of iodine in the sensitization is thought to be helping recrystallization of PbSe grains and the resultant redistribution of oxygen atoms in the effective atomic sites.

Paper Details

Date Published: 19 September 2016
PDF: 11 pages
Proc. SPIE 9974, Infrared Sensors, Devices, and Applications VI, 997405 (19 September 2016); doi: 10.1117/12.2237284
Show Author Affiliations
Youngjoon Suh, Korea Institute of Science and Technology (Korea, Republic of)
Sang-Hee Suh, Korea Institute of Science and Technology (Korea, Republic of)


Published in SPIE Proceedings Vol. 9974:
Infrared Sensors, Devices, and Applications VI
Paul D. LeVan; Ashok K. Sood; Priyalal Wijewarnasuriya; Arvind I. D'Souza, Editor(s)

© SPIE. Terms of Use
Back to Top