Microwave surface resistance of high Tc superconducting films
Author(s): Prakash R. Apte; R. Pinto; Dhananjay Kumar; R. Vijayaraghavan
Format Member Price Non-Member Price
PDF $17.00 $21.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

The surface resistance, Rs, at microwave frequencies has been an important qualification parameter for high temperature superconductor (HTS) thin films. HTS thin films with low Rs have been realized on many substrates, and many groups have realized Rs values in the range 300 - 400 (mu) (Omega) at 10 GHz at 77 K with YBa2Cu3O7-(delta ) (YBCO) films on <100> LaAlO3 substrates. Both microstrip resonator and parallel plate resonator techniques are being used to measure Rs values of HTS thin films. It has been observed that the value of Rs at given frequency and temperature critically depends upon the epitaxial quality and granularity of the films. For example, YBCO films grown on <100> MgO have been found to be granular and weak link limited with a significant microwave power dependence of Rs. On the other hand, YBCO films insitu grown on <100> LaAlO3 have shown better epitaxy with low Rs. This is obviously due to the much better lattice match of YBCO with <100> LaAlO3 if the targets used for laser deposition are doped with Ag. Extensive work carried out in our laboratory has shown that a Ag-doping level of around 5 wt.% in YBCO is the optimum which results in YBCO films of much improved quality. We have realized Ag-doped YBCO films with Jc values of 6 - 8 X 106 Acm-2 at 77 K and a low Rs value of 210 (mu) (Omega) at 10 GHz at 77 K on <100> LaAlO3. Both these values are the best realized on LaAlO3 to date. What is equally important is the fact that with Ag-doping the reproducibility of the epitaxial quality of the films improves significantly. This has been found to be due to the enhanced oxygenation of films during growth and the surfactant effect of Ag. Experiments have shown that even the optimum temperature for insitu growth in reduced considerably by Ag-doping. It must be mentioned, however, that the only negative aspect of Ag-doping is the higher microwave residual surface resistance, Rres, observed in these films at (very) low temperatures. This is obviously due to the presence of Ag in the grain boundaries which gives rise to a metallic contribution to Rs which appears as Rres. Nevertheless, Ag-doped YBCO films have been found to be superior to undoped films both due to their higher stability and lower Rs at 77 K, a temperature at which HTS devices are expected to operate.

Paper Details

Date Published: 1 September 1995
PDF: 13 pages
Proc. SPIE 2559, High-Temperature Microwave Superconductors and Applications, (1 September 1995); doi: 10.1117/12.218169
Show Author Affiliations
Prakash R. Apte, Tata Institute of Fundamental Research (India)
R. Pinto, Tata Institute of Fundamental Research (India)
Dhananjay Kumar, Tata Institute of Fundamental Research (India)
R. Vijayaraghavan, Tata Institute of Fundamental Research (India)


Published in SPIE Proceedings Vol. 2559:
High-Temperature Microwave Superconductors and Applications
James D. Hodge, Editor(s)

© SPIE. Terms of Use
Back to Top