Characterization of excimer lamp photo-deposited ultrathin oxynitride films
Author(s): S. Lynch; Gerard M. O'Connor; Gabriel M. Crean; J. Y. Zhang; Zsolt Geretovszky; Philippe Bergonzo; Ian W. Boyd
Format Member Price Non-Member Price
PDF $17.00 $21.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Excimer lamp deposited ultra-thin (< 250 angstrom) silicon dioxide and silicon oxynitride films were characterized using spectroscopic ellipsometry (SE) and Fourier transform infrared (FTIR) spectroscopy. SE analysis of the photo-deposited SiO2 films revealed no variation in the refractive index (n) of the films for deposition temperatures of 200 degree(s)C and 300 degree(s)C. Using a Bruggeman effective medium approximation (EMA), SE analysis was employed to determine both the silicon oxynitride layer thicknesses and compositions as a function of deposition temperatures and gas ratio, defined as (N2O/(N2O + NH3)). From this analysis the optical properties of the silicon oxynitride thin films were extracted. It was observed that the refractive index for the 200 degree(s)C and 300 degree(s)C series of samples decreased from n equals 1.81 to 1.46 and n equals 1.72 to 1.46 respectively as a function of increasing gas flow ratio. FTIR analysis revealed spectral features characteristic of Si-O, Si-N, Si-H and N-H bonding. The most significant feature in all recorded spectra was a mixed spectral absorption band ranging from 800 cm-1 to 1300 cm-1. Both the integrated band area and peak wavenumber of this absorption band was found to be sensitive to the degree of nitridation and layer thickness of the thin films. The N-H stretching bond density was calculated from the N-H peak at 3360 cm-1 using appropriate calibration factors. A slight decrease in the N-H bond density with increasing gas flow rate was observed. This variation in bond density was significantly less than that observed for PECVD silicon oxynitride films.

Paper Details

Date Published: 10 April 1995
PDF: 9 pages
Proc. SPIE 2403, Laser-Induced Thin Film Processing, (10 April 1995); doi: 10.1117/12.206261
Show Author Affiliations
S. Lynch, National Microelectronics Research Ctr. (Ireland)
Gerard M. O'Connor, National Microelectronics Research Ctr. (Ireland)
Gabriel M. Crean, National Microelectronics Research Ctr. (Ireland)
J. Y. Zhang, Univ. College London (United Kingdom)
Zsolt Geretovszky, Univ. College London (United Kingdom)
Philippe Bergonzo, Univ. College London (United Kingdom)
Ian W. Boyd, Univ. College London (United Kingdom)


Published in SPIE Proceedings Vol. 2403:
Laser-Induced Thin Film Processing
Jan J. Dubowski, Editor(s)

© SPIE. Terms of Use
Back to Top