Nickel oxide growth on Si (111), c-Al2O3 and FTO/glass by pulsed laser deposition
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

NiO was grown on Si (111), c-Al2O3 and FTO/glass substrates by pulsed laser deposition (PLD). X-Ray Diffraction (XRD) and scanning electron microscope (SEM) studies revealed that layers grown on c-Al2O3 were fcc NiO with a dense morphology of cubic grains that were strongly (111) oriented along the growth direction. The relatively low ω rocking curve linewidth, of 0.12°suggests that there may have been epitaxial growth on the c-Al2O3 substrate. XRD and SEM indicated that films grown on Si (111) were also fcc NiO, with cubic grains, but that the grain orientation was random. This is consistent with the presence of an amorphous SiO2 layer at the surface of the Si substrate, which precluded epitaxial growth. NiO grown at lower temperature (200°C) on temperature-sensitive FTO/glass substrates showed no evidence of crystallinity in XRD and SEM studies. After flash annealing in air, however, peaks characteristic of randomly oriented fcc NiO appeared in the XRD scans and the surface morphology became more granular in appearance. Such layers appear promising for the development of future dye-sensitised solar cell devices based on NiO grown by PLD.

Paper Details

Date Published: 8 March 2014
PDF: 7 pages
Proc. SPIE 8987, Oxide-based Materials and Devices V, 89872P (8 March 2014); doi: 10.1117/12.2057620
Show Author Affiliations
V. E. Sandana, Nanovation (France)
D. J. Rogers, Nanovation (France)
F. Hosseini Teherani, Nanovation (France)
P. Bove, Nanovation (France)
R. McClintock, Northwestern Univ. (United States)
M. Razeghi, Northwestern Univ. (United States)


Published in SPIE Proceedings Vol. 8987:
Oxide-based Materials and Devices V
Ferechteh H. Teherani; David C. Look; David J. Rogers, Editor(s)

© SPIE. Terms of Use
Back to Top