Dynamical behavior of photoluminescence of fullerene C60
Author(s): Jie Song; Feiming Li; Shixiong Qian; Yufen Li; Wen-Ji Peng; Jianying Zhou; Zhenxin Yu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Using a picosecond excitation source and a time-resolved streak camera detection system, we have observed the time-resolved photoluminescence spectra of C60 from toluene solution at room temperature and from thin film at both room temperature and 77 K. For C60 solution, a photoluminescence peak at about 730 nm was detected at room temperature and its decay time was determined to be 1.1 ns. For C60 film, the photoluminescence peak was at about 730 nm at 77 K and 740 nm at room temperature, respectively. Its time decay behavior changed from a slow process with decay time of 0.9 ns to a fast process which was fitted well to a double exponential of decay times of (tau) 1 equals 0.087 ns, (tau) 2 equals 0.68 ns. Some relaxation mechanisms are suggested in explaining this phenomenon.

Paper Details

Date Published: 28 November 1994
PDF: 7 pages
Proc. SPIE 2284, Fullerenes and Photonics, (28 November 1994); doi: 10.1117/12.196127
Show Author Affiliations
Jie Song, Fudan Univ. (Japan)
Feiming Li, Fudan Univ. (China)
Shixiong Qian, Fudan Univ. (China)
Yufen Li, Fudan Univ. (China)
Wen-Ji Peng, Zhongshan Univ. (China)
Jianying Zhou, Zhongshan Univ. (China)
Zhenxin Yu, Zhongshan Univ. (China)


Published in SPIE Proceedings Vol. 2284:
Fullerenes and Photonics
Zakya H. Kafafi, Editor(s)

© SPIE. Terms of Use
Back to Top