Transmission electrom microscopy (TEM) defect studies of molecular beam epitaxy (MBE) grown ZnSxSe1-x/GaAs interface
Author(s): Li-Hsin Kuo; Lourdes Salamanca-Riba; G. E. Hofler; Bor-Jen Wu; Michael A. Haase
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Both Shockley and Frank partial dislocations originating at the ZnSxSe1-x/GaAs interface were observed with defect densities in the range less than 5 X 104/cm2 to approximately 1 X 108/cm2 for samples grown under different conditions. These faulted defects act as heterogeneous nucleation sites for the generation of 60 degree(s) misfit dislocations. A very low density of Shockley partial dislocations was obtained in ZnSxSe1-x films grown by the layer-by-layer mode on GaAs substrates. Also, the density of Frank partial dislocations was decreased by exposing the As- stabilized GaAs surface to Zn for 1-2 minutes prior to the growth of the ZnSxSe1-x epilayers. These samples contained a defect density lower than 5 X 104/cm2. A Ga2Se3 compound existing at the ZnSxSe1-x/GaAs interface is thought to be the source of the Frank partial dislocations.

Paper Details

Date Published: 13 July 1994
PDF: 9 pages
Proc. SPIE 2228, Producibility of II-VI Materials and Devices, (13 July 1994); doi: 10.1117/12.179653
Show Author Affiliations
Li-Hsin Kuo, Univ. of Maryland/College Park (United States)
Lourdes Salamanca-Riba, Univ. of Maryland/College Park (United States)
G. E. Hofler, 3M Photonics Research Lab. (United States)
Bor-Jen Wu, 3M Photonics Research Lab. (United States)
Michael A. Haase, 3M Photonics Research Lab. (United States)


Published in SPIE Proceedings Vol. 2228:
Producibility of II-VI Materials and Devices
Herbert K. Pollehn; Raymond S. Balcerak, Editor(s)

© SPIE. Terms of Use
Back to Top