Modified polyimide side-chain polymers with high glass transition temperatures for nonlinear optical applications
Author(s): B. Zysset; M. Ahlheim; M. Staehelin; F. Lehr; Philippe Pretre; P. Kaatz; Peter Guenter
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Novel modified polyimide polymers with nonlinear optical chromophores as pendent side groups show high glass transition temperatures and large nonlinear optical coefficients up to d33 equals 78 pm/V at (lambda) equals 1313 nm (electro-optic coefficient r33 equals 18 pm/V). Due to the high glass transition temperatures of up to 190 $DEGC an excellent long term stability of the nonlinearity results. Extrapolation from measurements at elevated temperatures predict long term stabilities of the nonlinearity in excess of tens of years at 80 $DEGC and hundreds to thousands of years at room temperature. The structural (molecular weight, glass transition temperature) and optical (refractive index, nonlinearity) properties of these polyimides can easily be varied which allows to taylor active layer and buffer layer materials.

Paper Details

Date Published: 16 December 1993
PDF: 8 pages
Proc. SPIE 2025, Nonlinear Optical Properties of Organic Materials VI, (16 December 1993); doi: 10.1117/12.165243
Show Author Affiliations
B. Zysset, SANDOZ Optoelectronics Research (France)
M. Ahlheim, SANDOZ Optoelectronics Research (France)
M. Staehelin, SANDOZ Optoelectronics Research (France)
F. Lehr, SANDOZ Optoelectronics Research (France)
Philippe Pretre, Swiss Federal Institute of Technology (Switzerland)
P. Kaatz, Swiss Federal Institute of Technology (Switzerland)
Peter Guenter, Swiss Federal Institute of Technology (Switzerland)


Published in SPIE Proceedings Vol. 2025:
Nonlinear Optical Properties of Organic Materials VI
Gustaaf R. Moehlmann, Editor(s)

© SPIE. Terms of Use
Back to Top