Laser deposition of cubic and hexagonal structured CdS thin films
Author(s): Xing Wu Wang; Robert J. Noble; D. J. Finnigan; F. Spitulnik; P. McGinnis; L. P. Fu; Athos P. Petrou
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A Nd:YAG LASER operating at 1.064 micrometers was used to deposit CdS thin films on glass and GaAs (100) substrates. Depending on the substrate temperature, the as-deposited films were either cubic or hexagonal dominant. At a substrate temperature of approximately 200 degree(s)C, predominantly cubic structured films were grown while at approximately 400 degree(s)C the hexagonal phase was formed. The films were in the stoichiometric ratio of 1:1 for Cd:S. The surface of the films were optically smooth. Optical transmission revealed the room temperature absorption edge for the cubic films was close to 515 nm, and that of the hexagonal films was approximately 500 nm. At a temperature of 10 K, the absorption edge of the cubic film was 502 nm. Raman spectrum studies revealed the locations of the first two longitudinal optical (LO) modes for the cubic films were close to that of the hexagonal films.

Paper Details

Date Published: 2 March 1993
PDF: 12 pages
Proc. SPIE 1793, Integrated Optics and Microstructures, (2 March 1993); doi: 10.1117/12.141211
Show Author Affiliations
Xing Wu Wang, Alfred Univ. (United States)
Robert J. Noble, Alfred Univ. (United States)
D. J. Finnigan, Alfred Univ. (United States)
F. Spitulnik, Alfred Univ. (United States)
P. McGinnis, Alfred Univ. (United States)
L. P. Fu, SUNY/Buffalo (United States)
Athos P. Petrou, SUNY/Buffalo (United States)


Published in SPIE Proceedings Vol. 1793:
Integrated Optics and Microstructures
Massood Tabib-Azar; Dennis L. Polla, Editor(s)

© SPIE. Terms of Use
Back to Top