Anisotropy in polyetheretherketone films
Author(s): Jasmin Althaus; Hans Deyhle; Bert Müller; Oliver Bunk; Per Magnus Kristiansen
Format Member Price Non-Member Price
PDF $20.00 $25.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Optical measurements reveal the preferential orientation of nanostructures within polymer films, which results from the fabrication process including mechanical and thermal treatments. As the wavelength of the incident light is generally much larger than the characteristic dimensions of the molecular arrangement in semi-crystalline or amorphous polymers, the optical signal originates not directly from the nanostructure of the polymers. Linear dichroism measurements were correlated with synchrotron radiation-based x-ray scattering data on commercially available polyetheretherketone (PEEK) thin films (12 to 50 μm). Annealing changed the structure of amorphous films to semi-crystalline ones associated with the measured linear dichroism. The intensity of the measured anisotropic signal depended on the film thickness. While for wavelengths between 450 and 1100 nm the transmission was higher when the polarizer was parallel to the machine direction, for larger wavelengths maximum transmission was observed with the polarizer perpendicular to the machine direction indicating excitations parallel and perpendicular to the PEEK molecule axis, respectively. Annealing PEEK films at temperatures between 160 and 240°C decreased the transmission at 540 nm by a factor of two, whereas the anisotropy remained constant. x-ray scattering revealed strongest anisotropy for a periodicity of 15 nm in the machine direction of the cast film extrusion process. The long-range order of amorphous and semi-crystalline entities can explain the x-ray scattering data and the related optical anisotropy of casted PEEK films.

Paper Details

Date Published: 2 July 2012
PDF: 12 pages
J. Nanophoton. 6(1) 063510 doi: 10.1117/1.JNP.6.063510
Published in: Journal of Nanophotonics Volume 6, Issue 1
Show Author Affiliations
Jasmin Althaus, Basel Univ. Hospital (Switzerland)
Hans Deyhle, Basel Univ. Hospital (Switzerland)
Bert Müller, Basel Univ. Hospital (Switzerland)
Oliver Bunk, Paul Scherrer Institut (Switzerland)
Per Magnus Kristiansen, FH Aargau Nordwestschweiz - Letzte Aktualisierung (Switzerland)


© SPIE. Terms of Use
Back to Top