Al2O3−BaTiO3 nanolaminates fabricated by multistationary target pulsed laser deposition with in situ ellipsometry
Author(s): John G. Jones; John J. Boeckl; Steven R. Smith; Gerald R. Landis; Neil R. Murphy; Zhongqiang Hu; Cynthia T. Bowers; Charles Ed Stutz
Format Member Price Non-Member Price
PDF $20.00 $25.00

Paper Abstract

Layered oxide materials having alternating repeated layer thicknesses of 10 nm or less are difficult to make, especially with sharp interfaces. Nanostructured thin films having repeated layers of two different oxide materials were obtained by using pulsed laser deposition and two independent stationary targets consisting of Al 2 O 3 and BaTiO 3 . Desired thicknesses were achieved by using a specific number of pulses from a 248-nm KrF excimer laser, at an energy of 450    mJ / pulse , a galvanometer mirror system, and a background pressure of oxygen. Trends in material properties were identified by systematically varying the number of pulses for multiple nanostructured thin films and comparing the resulting properties measured using in-situ spectroscopic ellipsometry and ex-situ capacitance measurements, including relative permittivity and loss. Four films were deposited with a goal of having 0.25-, 1-, 4-, and 10-nm thick layers, and each 220    nm thick. Ellipsometry data were modeled in situ to calculate thickness, n and k . A representative transmission electron microscopy measurement was also collected for the 10-nm sample with corresponding x-ray photoelectron spectroscopy and energy disperive x-ray spectroscopy. Ellipsometry and capacitance measurements were all performed on each of the samples, with one sample having calculated impedance greater than 30 GOhm at 0.001 Hz.

Paper Details

Date Published: 20 April 2017
PDF: 14 pages
J. Nanophoton. 11(4) 043506 doi: 10.1117/1.JNP.11.043506
Published in: Journal of Nanophotonics Volume 11, Issue 4
Show Author Affiliations
John G. Jones, Air Force Research Lab. (United States)
John J. Boeckl, Air Force Research Lab. (United States)
Steven R. Smith, Univ. of Dayton Research Institute (United States)
Gerald R. Landis, Univ. of Dayton Research Institute (United States)
Neil R. Murphy, Air Force Research Lab. (United States)
Zhongqiang Hu, Universal Technology Corp. (United States)
Cynthia T. Bowers, Wright State Univ. (United States)
Charles Ed Stutz, Air Force Research Lab. (United States)


© SPIE. Terms of Use
Back to Top