Investigation of indium gallium nitride facet-dependent nonpolar growth rates and composition for core–shell light-emitting diodes
Author(s): Ionut Gîrgel; Paul R. Edwards; Emmanuel Le Boulbar; Pierre-Marie Coulon; Suman Lata Sahonta; Duncan W. E. Allsopp; Robert W. Martin; Colin J. Humphreys; Philip A. Shields

Paper Abstract

Core–shell indium gallium nitride (InGaN)/gallium nitride (GaN) structures are attractive as light emitters due to the large nonpolar surface of rod-like cores with their longitudinal axis aligned along the c-direction. These facets do not suffer from the quantum-confined Stark effect that limits the thickness of quantum wells and efficiency in conventional light-emitting devices. Understanding InGaN growth on these submicron three-dimensional structures is important to optimize optoelectronic device performance. In this work, the influence of reactor parameters was determined and compared. GaN nanorods (NRs) with both {11-20}a-plane and {10-10}m-plane nonpolar facets were prepared to investigate the impact of metalorganic vapor phase epitaxy reactor parameters on the characteristics of a thick (38 to 85 nm) overgrown InGaN shell. The morphology and optical emission properties of the InGaN layers were investigated by scanning electron microscopy, transmission electron microscopy, and cathodoluminescence hyperspectral imaging. The study reveals that reactor pressure has an important impact on the InN mole fraction on the {10-10}m-plane facets, even at a reduced growth rate. The sample grown at 750°C and 100 mbar had an InN mole fraction of 25% on the {10-10} facets of the NRs.

Paper Details

Date Published: 7 March 2016
PDF: 11 pages
J. Nanophoton. 10(1) 016010 doi: 10.1117/1.JNP.10.016010
Published in: Journal of Nanophotonics Volume 10, Issue 1
Show Author Affiliations
Ionut Gîrgel, Univ. of Bath (United Kingdom)
Paul R. Edwards, Univ. of Strathclyde (United Kingdom)
Emmanuel Le Boulbar, Univ. of Bath (United Kingdom)
Pierre-Marie Coulon, Univ. of Bath (United Kingdom)
Suman Lata Sahonta, Univ. of Cambridge (United Kingdom)
Duncan W. E. Allsopp, Univ. of Bath (United Kingdom)
Robert W. Martin, Univ. of Strathclyde (United Kingdom)
Colin J. Humphreys, Univ. of Cambridge (United Kingdom)
Philip A. Shields, Univ. of Bath (United Kingdom)


© SPIE. Terms of Use
Back to Top