Author(s): Thomas E. Wilson; Konstantin A. Korolev; Nathaniel A. Crow
Format Member Price Non-Member Price
PDF $20.00 $25.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Recently published reports in the literature for bilayer lift-off processes have described recipes for the patterning of metals that have recommended metal-ion-free developers, which do etch aluminum. We report the first measurement of the dissolution rate of a commercial lift-off resist (LOR) in a sodium-based buffered commercial developer that does not etch aluminum. We describe a reliable lift-off recipe that is safe for multiple process steps in patterning thin (<100  nm) and thick aluminum devices with micron-feature sizes. Our patterning recipe consists of an acid cleaning of the substrate, the bilayer (positive photoresist/LOR) deposition and development, the sputtering of the aluminum film along with a palladium capping layer and finally, the lift-off of the metal film by immersion in the LOR solvent. The insertion into the recipe of postexposure and sequential develop-bake-develop process steps are necessary for an acceptable undercut. Our recipe also eliminates any need for accompanying sonication during lift-off that could lead to delamination of the metal pattern from the substrate. Fine patterns were achieved for both 100-nm-thick granular aluminum/palladium bilayer bolometers and 500-nm-thick aluminum gratings with 6-μm lines and 4-μm spaces.

Paper Details

Date Published: 20 January 2015
PDF: 5 pages
J. Micro/Nanolith. MEMS MOEMS 14(1) 014501 doi: 10.1117/1.JMM.14.1.014501
Published in: Journal of Micro/Nanolithography, MEMS, and MOEMS Volume 14, Issue 1
Show Author Affiliations
Thomas E. Wilson, Marshall Univ. (United States)
Konstantin A. Korolev, Marshall Univ. (United States)
Nathaniel A. Crow, Marshall Univ. School of Medicine (United States)

© SPIE. Terms of Use
Back to Top