Three-dimensional digital image correlation to quantify deformation and crack-opening displacement in ductile aluminum under mixed-mode I/III loading
Author(s): Michael A. Sutton; J. H. Yan; Xiaomin Deng; C. S. Cheng; P. Zavattieri
Format Member Price Non-Member Price
PDF $20.00 $25.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Fractures in ductile thin-sheet structures, such as a fuselage or automobile panels, often occur under complex loading conditions. In particular, under remote mixed-mode I/III loading conditions, a cracked structure is subjected to a combination of in-plane tension and large out-of-plane tearing deformation, which may lead to crack tip fields consisting of all three fracture modes (modes I, II, and III). Understanding such fracture events in ductile materials is an important component of the structural integrity analysis of load-bearing structures containing ductile, thin sheets. Due to the complex nature of mixed-mode I/III fracture in ductile thin-sheet materials, reports of experimental investigations are very limited in the literature. We configure three-dimensional digital image correlation (3D-DIC) systems to acquire full-field deformations during the loading and stable tearing processes. The full-field deformation measurements are used to characterize the stable crack extension behavior of an aluminum alloy undergoing quasistatic and dynamic mixed-mode I/III loading. Results confirm that 3D-DIC is an excellent methodology for measuring 3-D deformations in the presence of large out-of-plane warping and motion, both dynamically and statically. Data obtained during the fracture process indicate that the introduction of a mode III component into the loading process alters the crack tip displacement and strain fields relative to those measured in the nominally mode I loading. Furthermore, the measured crack-opening displacement (COD) values during quasistatic and impact mixed-mode I/III fracture show that (1) COD is nearly constant for crack extension beyond 2 mm and (2) COD under combined-mode I/III loading is four times larger than observed during mixed-mode I/II or mode I fracture of the same material, indicating that the magnitude of the critical COD is a function of loading mode in highly ductile, thin-sheet materials.

Paper Details

Date Published: 1 May 2007
PDF: 17 pages
Opt. Eng. 46(5) 051003 doi: 10.1117/1.2741279
Published in: Optical Engineering Volume 46, Issue 5
Show Author Affiliations
Michael A. Sutton, Univ. of South Carolina (United States)
J. H. Yan, Univ. of South Carolina (United States)
Xiaomin Deng, Univ. of South Carolina (United States)
C. S. Cheng, General Motors Corp. (United States)
P. Zavattieri, General Motors Corp. (United States)


© SPIE. Terms of Use
Back to Top